I hope this helps some of you. I've seen in some recent posts that some of you are less than confident with your welding skills. If your using a 110 volt mig, you should be running .023 wire with a 75/25 argon co2 mix.If your using flux core (inner shield) your weld will be sufficient but not nearly as pretty as with gas.assuming its .030 or .035 wire.For those using a 220 volt welder its okay to use a heavier wire such as .030 or .035, but again use a 75/25 argon co2 mix. Wire speed and heat are the key factors in the way the weld will look, if you lift the door on the wire side of the machine it will guide you in what gauge,speed and heat you should set your macine at.For 110 users make sure your on a dedicated 20 amp circuit. If anyone has any questions feel free to PM me. hope this helps.
-
Hey Guest!
British Car Forum has been supporting enthusiasts for over 25 years by providing a great place to share our love for British cars. You can support our efforts by upgrading your membership for less than the dues of most car clubs. There are some perks with a member upgrade!**Upgrade Now**
(PS: Upgraded members don't see this banner, nor will you see the Google ads that appear on the site.)
-
When posting a classified ad, you MUST select a prefix from the drop-down next to the subject line. If you don't you will get an error and your ad will not be posted!
Welding 101.