    If you appreciate British Car Forum and our 25 years of supporting British car enthusiasts with technical and anicdotal information, collected from our thousands of great members, please support us with a low-cost subscription. You can become a supporting member for less than the dues of most car clubs.
    There are some perks with a member upgrade!
    **Upgrade Now**
    (PS: Subscribers don't see this gawd-aweful banner
Tips
Tips

Light crucible needed for melting aluminum

Share this page

G

Guest

Guest
Guest
Offline
I need a light material with fairly high thermal conductivity to melt aluminum in. Most guys use steel pipe but that's too heavy for what I'm doing. I've useed thin steel but it burns through too quickly. I need soemthing that'll take high temps with large thermal shocks that will be lighter than 1/4" thick steel pipe.

Crucible size will be around 3-4" in diameter and about 4-5" tall.
 
You've got a ceramics expert on-site, fercryinoutloud... toss one onna wheel, fire it without glaze and Cuthbert's th' parrot of yer great aunt!

Whadda ya think gold casting is done with?
 
I know it's larger but suspect it'd work better than what he's tried so-far. ;)

Aluminum melts at relatively lower temps than gold, too. 1200-ish °F vs. <2000°F for gold. IIRC
 
Last edited:
It won't withstand the shock Doc. Even with raku clay with a much slower temp rate gives us trouble much less a full-blast furnace. I wondered about stainless if it will withstand multiply firings at a minimal thickness. I don't like stainless' thermal conductivity. I wonder about copper? I may just have to use steel. Livin' on the edge here as my process/technique is all uncharted territory. Gotta fab up all my equipment. Biggest problem is, if a cruible fails on me my goose is cooked, literaly...
 
Stainless should work well at 1200. We fire waste enamel at work in SS mixing bowls up to 1600. We use them many times over and they are cheap.
 
Just regular mixing bowls. Thin and cheap. You could use pet bowls for smaller stuff. Assuming that you are using an electric kiln, you shouldn't have a problem.
 
Well, yes and no. My furnace is very similar (large feed bucket) however; his crucible is too heavy and is grabbed from the top. I will have to make a vice-grip like clamp with a heat shield to grab it close in from the side. I may still have to go with steel. I just hate to use something that heavy.
 
I'd reccomend inconel (Spelling?) but that ain't light either. nor is it cheap.
 